EFFECT OF SOOT PARTICLE SIZE ON FOUR BALL METALLIC WEAR USING ELECTRON MICROSCOPY IMAGE ANALYSIS
Preechar Karin1, Warawut Amornprapa1, Park Watanawongskorn1, Eakkawut Saenkhumvong1, Chinda Charoenphonphanich1, Katsunori Hanamura2
1King Mongkut’s Institute of Technology Ladkrabang
2Tokyo Institute of Technology
PDF Links Corresponding Author.  Preechar Karin , Email. preechar.ka@kmitl.ac.th
ABSTRACT
The impact of soot primary nanoparticles affecting metal wear was investigated. The commercial Carbon Black (CB) with different primary particle sizes were mixed with the engine oil for simulating soot contamination. The physical properties of carbon black including density and hardness were calculated using Transmission Electron Microscopy (TEM) image analysis. The metallic wear test was evaluated by using a Four-ball wear tester. After the tests, the ball surfaces were inspected by utilizing High-Resolution Optical Microscope (OM), Scanning Electron Microscope (SEM) and Energy Dispersive X-ray spectroscopy (EDX) analysis. Based on a Four-ball wear test, the 1 % by weight of carbon black contamination shows a bit higher average wear scar diameter (WSD), but the surface roughness is reduced. SEM micrograph of metallic wear scar for the engine oil without soot shows the area of grooves, plastic deformation and subsurface crack. On the other hand, when carbon black is added to the oil, it can be seen that there are many deep grooves along with the sliding direction. The relationship of calculated oil film thickness, primary nanoparticle size distribution, carbon atom density of soot and hardness is clearly explained metallic wear mechanisms.
Key Words: Soot, Engine oil, Metallic wear, Electron microscopy, Nanostructure, Carbon black

Editorial Office
21 Teheran-ro 52-gil, Gangnam-gu, Seoul 06212, Korea
TEL: +82-2-564-3971   FAX: +82-2-564-3973   E-mail: manage@ksae.org
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Society of Automotive Engineers.                 Developed in M2PI
Close layer
prev next